Thermomechanical analysis of fatigue degradations in carbon epoxy laminates

Résumé

The tensile fatigue behavior of a high stress carbon fiber epoxy-matrix composite laminates was examined at room temperature. Tension-tension cyclic fatigue tests were also conducted under load control at a sinusoidal frequency of 5 Hz to obtain stress-fracture cycles (S-N) relationship. The fatigue limits of the different lay-up tested were found and compared with the data resulting from self-heating tests on the same materials. This comparison reveals a good accordance between the two methods of fatigue limit determination. A macroscopic fatigue damage evolution law is then proposed to reproduce the experimental data.
Fichier principal
Vignette du fichier
Westphal2012.pdf (808.55 Ko) Télécharger le fichier
Origine Fichiers produits par l'(les) auteur(s)

Dates et versions

hal-01009046 , version 1 (29-04-2024)

Identifiants

  • HAL Id : hal-01009046 , version 1

Citer

Ophélie Westphal, Laurent Gornet, Laurent Stainier, Patrick Rozycki. Thermomechanical analysis of fatigue degradations in carbon epoxy laminates. 15th European Conference on Composite Materials - ECCM15, 2012, Venice, Italy. ⟨hal-01009046⟩
86 Consultations
1 Téléchargements

Partager

Gmail Mastodon Facebook X LinkedIn More